Effect of joint contamination on the quality of butt-fused high-density polyethylene (HDPE) pipe joints
Butt fusion is an effective method for joining high-density polyethylene (HDPE) pipe on job sites. However, there is lack of quantitative methods to evaluate pipe joint quality. The objective of this study was to develop such a quantitative approach to determine the effect of joint contamination on...
Gespeichert in:
Veröffentlicht in: | Canadian journal of civil engineering 2002-10, Vol.29 (5), p.787-798 |
---|---|
Hauptverfasser: | , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Butt fusion is an effective method for joining high-density polyethylene (HDPE) pipe on job sites. However, there is lack of quantitative methods to evaluate pipe joint quality. The objective of this study was to develop such a quantitative approach to determine the effect of joint contamination on the quality of the fused joints. The study included testing a total of 21 butt-fused HDPE pipe joints that were made under different dust conditions. The results of the tests were then used to determine the effect of dust contamination on the quality of the fused joints. Microscopic examination of the fracture surfaces of the test specimens showed that not all the contaminants at the welding interface were squeezed out into the beads formed during the fusion process. Four failure modes were identified and a failure criterion was established to categorize the quality of a fused joint into four grades: bad, poor, good, and excellent. Among the properties of the materials considered, tensile energy to break (TEB) and maximum strain were found to be the most acceptable parameters for distinguishing between joints of different quality. Furthermore, the results showed that under optimum joining conditions, the quality of butt-fused joints can be as good as that of the parent pipe.Key words: polyethylene pipe, butt fusion, joint contamination, tensile energy to break, failure criterion. |
---|---|
ISSN: | 0315-1468 1208-6029 |
DOI: | 10.1139/l02-078 |