Room temperature multiferroic properties of (Fex, Sr1−x)TiO3 thin films

This letter reports the structural, dielectric, ferroelectric, and magnetic properties of Fe substituted SrTiO3 thin films in room temperature. The structural data obtained from x-ray diffraction indicates that (Fex,Sr1−x)TiO3, the so called FST, transforms from pseudocubic to tetragonal structures...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Applied physics letters 2014-09, Vol.105 (10)
Hauptverfasser: Kim, Kyoung-Tae, Kim, Cheolbok, Fang, Sheng-Po, Yoon, Yong-Kyu
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:This letter reports the structural, dielectric, ferroelectric, and magnetic properties of Fe substituted SrTiO3 thin films in room temperature. The structural data obtained from x-ray diffraction indicates that (Fex,Sr1−x)TiO3, the so called FST, transforms from pseudocubic to tetragonal structures with increase of the Fe content in SrTiO3 thin films, featuring the ferroelectricity, while vibrating sample magnetometer measurements show magnetic hysteresis loops for the samples with low iron contents indicating their ferromagnetism. The characterized ferroelectricity and ferromagnetism confirms strong multiferroitism of the single phase FST thin films in room temperature. Also, an FST thin film metal-insulator-metal multiferroic capacitor has been fabricated and characterized in microwave frequencies between 10 MHz and 5 GHz. A capacitor based on Fe0.1Sr0.9TiO3 with a thickness of 260 nm shows a high electric tunability of 18.6% at 10 V and a maximum magnetodielectric value of 1.37% at 0.4 mT with a loss tangent of 0.021 at 1 GHz. This high tuning and low loss makes this material as a good candidate for frequency agile microwave devices such as tunable filters, phase shifters, and antennas.
ISSN:0003-6951
1077-3118
DOI:10.1063/1.4894850