Structure refinement of Ba0.5Sr0.5Co0.8Fe0.2O3-d as cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFC)
Ba0.5Sr0.5Co0.8Fe0.2O3-δ was successfully prepared using modified solid-state synthesis routes. The lowest temperature to obtained single phase of Ba0.5Sr0.5Co0.8Fe0.2O3-δ is about 900°C for 15 hours. Longer period of time are required compared to only 5 hours at 950°C as established in literatures....
Gespeichert in:
Hauptverfasser: | , , |
---|---|
Format: | Tagungsbericht |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Ba0.5Sr0.5Co0.8Fe0.2O3-δ was successfully prepared using modified solid-state synthesis routes. The lowest temperature to obtained single phase of Ba0.5Sr0.5Co0.8Fe0.2O3-δ is about 900°C for 15 hours. Longer period of time are required compared to only 5 hours at 950°C as established in literatures. The X-ray Diffraction (XRD) data confirmed that Ba0.5Sr0.5Co0.8Fe0.2O3-δ is formed a cubic perovskite with the space group of Pm-3m. The lattice parameters of Ba0.5Sr0.5Co0.8Fe0.2O3-δ are a = 3.990 (1) Å and unit cell volume is V = 63.5 (1) Å3. The Rietveld refinement of XRD data revealed that the crystal structure of Ba0.5Sr0.5Co0.8Fe0.2O3-δ slightly changes as a function of temperature. |
---|---|
ISSN: | 0094-243X 1551-7616 |
DOI: | 10.1063/1.4958787 |