Elaboration and Investigation of Metallic Coating with Inclusion of Potassium Polytitanate
The possibility of receiving of compositional Ni-P coating modified by potassium polytitanate was analyzed. An aqueous solution to obtain the composite coatings on the basis of nickel-phosphorus alloy modified by K2О·nTiO2 onto steel details of the friction knots was developed. The complex oxide K2О...
Gespeichert in:
Veröffentlicht in: | Solid state phenomena 2018-10, Vol.284, p.1140-1143 |
---|---|
Hauptverfasser: | , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The possibility of receiving of compositional Ni-P coating modified by potassium polytitanate was analyzed. An aqueous solution to obtain the composite coatings on the basis of nickel-phosphorus alloy modified by K2О·nTiO2 onto steel details of the friction knots was developed. The complex oxide K2О·nTiO2 represents a layered material from the scaly form nanocrystals with 20-80 nm thick and "diameter" 280 nm. The velocity forming of the modified compositional Ni-P coating was investigated, and the optimal quantity of the introduced potassium polytitanate (8 g/l), as a modified compound into solution, was determined, too. The tribological characteristics and micro-hardness of the resulting coatings depending on the chemical composition of solution and surface state of the rider were investigated. |
---|---|
ISSN: | 1012-0394 1662-9779 1662-9779 |
DOI: | 10.4028/www.scientific.net/SSP.284.1140 |