Nanosecond laser-metal ablation at different ambient conditions

Ablation of metals under different ambient conditions and laser fluences, was investigated through series of experiments. A 1064nm, 6ns Nd:YAG laser was used to ablate 1mm thick metal targets with laser energy ranging from 2mJ to 300mJ. The experiments were designed to study the effect of material properties, laser fluence, ambient gas, and ambient pressure on laser-metal ablation. The first experiment was conducted under vacuum to study the effect of laser fluence and material properties on metal ablation, using a wide range of laser fluences (2J/cm2 up to 300J/cm2) and two different targets, Al and W. The second experiment was conducted at atmospheric pressure using two different ambient gases air and argon, to understand the effect of ambient gas on laser-metal ablation process. The third experiment was conducted at two different pressures (10Torr and 760Torr) using the same ambient gas to investigate the effect of ambient pressure on laser-metal ablation. To compare the different ablation processes, the amount of mass ablated, ablation depth, crater profile and melt formation were measured using White Light Profilometer (WLP). The experimental results show that at low laser fluence: the ablated mass, ablation depth, and height of molten layer follow a logarithmic function of the incident laser fluence. While, at high laser fluence they follow a linear function. This dependence on laser fluence was found to be independent on ambient conditions and irradiated material. The effect of ambient pressure was more pronounced than the effect of ambient gas type. Plasma shielding effect was found to be very pronounced in the presence of ambient gas and led to significant reduction in the total mass ablation. [Display omitted] •Erosion of metals using laser irradiation•Effect of laser fluence and material properties on erosion•Effect of ambient conditions (ambient gas and pressure) on erosion•Mass ablation, ablation profile and melt layer measurements