Study of the High Temperature Metallurgical Properties of On-Site Samples with Vanadium–Titanium Magnetite

In China, two typical vanadium–titanium magnetite ores were used as raw materials in iron making. In order to obtain the differences in the high temperature metallurgical properties of these ores, the phase and microstructure of on-site sinter, pellet, slag and laboratorial non-dripped slag were analyzed by XRD and SEM–EDS. The results show that the phases of two typical sinter and pellet have no significant changes, but the microstructures are different. The softening start temperature and softening zone of high chromium vanadium–titanium magnetite (HCVTM) burden are higher than ordinary vanadium–titanium magnetite (VTM) burden. The melting start temperature of HCVTM burden is higher and melting–dripping zone is smaller than VTM burden, which is beneficial to the blast furnace smelting. In addition, the calculation results using Factsage 7.0 are in accord with the experimental results. The primary crystal field of slag of HCVTM is the melilite, and the liquidus temperature is 1409.81 °C; the primary crystal field of slag of VTM is CaTiO 3 , and the liquidus temperature is 1418.51 °C.