Performance of Bi2O3/TiO2 prepared by sol-gel on p-Cresol degradation under solar and visible light

Photocatalytic degradation of p-Cresol was evaluated using the mixed oxide Bi 2 O 3 /TiO 2 (containing 2 and 20% wt. Bi 2 O 3 referred as TB2 and TB20) and was compared with bare TiO 2 under simulated solar radiation. Materials were prepared by the classic sol-gel method. All solids exhibited the anatase phase by X-ray diffraction (XRD) and Raman spectroscopy. The synthesized materials presented lower crystallite size and Eg value, and also higher surface area as Bi 2 O 3 amount was increased. Bi content was quantified showing near to 70% of theoretical values in TB2 and TB20. Bi 2 O 3 incorporation also was demonstrated by X-ray photoelectron spectroscopy (XPS). Characterization of mixed oxides suggests a homogeneous distribution of Bi 2 O 3 on TiO 2 surface. Photocatalytic tests were carried out using a catalyst loading of 1 g L −1 under simulated solar light and visible light. The incorporation of Bi 2 O 3 in TiO 2 improved the photocatalytic properties of the synthesized materials obtaining better results with TB20 than the unmodified TiO 2 under both radiation sources.