PPE-g-HDPE in high-performance poly(p-phenylene ether)/polyethylene blends: synthesis and compatibilization effects

Poly(p-phenylene ether) (PPE) grafted with high-density polyethylene (HDPE), to form PPE-g-HDPE graft copolymers, were prepared by Friedel-Crafts alkylation of vinyl terminated HDPEs onto PPE. High and low molecular weight (MW) vinyl terminated HDPE precursors were synthesized by coordination insert...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Polymer (Guilford) 2018-02, Vol.138, p.92-102
Hauptverfasser: Wang, Jun, Tsou, Andy H., Passino, Hillary L., Favis, Basil D.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Poly(p-phenylene ether) (PPE) grafted with high-density polyethylene (HDPE), to form PPE-g-HDPE graft copolymers, were prepared by Friedel-Crafts alkylation of vinyl terminated HDPEs onto PPE. High and low molecular weight (MW) vinyl terminated HDPE precursors were synthesized by coordination insertion polymerization with organometallic catalysts that favor beta-hydride transfer. Both types of copolymers are highly effective compatibilizers for PPE/HDPE blends when PPE is the minor phase. The symmetric PPE-g-HDPE copolymer with high MW grafted HDPE shows a somewhat higher efficacy at reducing the dispersed phase size and delaying the onset of PPE phase continuity. However, when HDPE is the minor phase, the asymmetric PPE-g-HDPE copolymer with low-molecular-weight grafted HDPE appears to be more effective at reducing particle anisotropy and at delaying the HDPE phase continuity onset. This delay in HDPE phase continuity onset, in turn, allows the retention of high-temperature PPE stiffness in the blends with 20 wt% HDPE. An examination of the glass transition temperatures indicates that the symmetric copolymer with higher HDPE MW appears to have a marked tendency to form micelles within PPE and thus is less effective at modifying the HDPE/PPE interface when PPE is the matrix. [Display omitted] •PPE-g-HDPE copolymers with high and low molecular weight HDPE grafts are synthesized.•Storage moduli of HDPE/PPE blends are significantly increased after compatibilization.•PPE-g-HDPE copolymers plasticize PPE and associate with HDPE at the interface.
ISSN:0032-3861
1873-2291
DOI:10.1016/j.polymer.2018.01.041