Synthesis and characterization of poly(2,6-dialkoxy-1,5-naphthylene)s with low dielectric constants

An efficient method to decrease dielectric constant ( ε ) of poly(2,6-dihydroxy-1,5-naphthylene) (PDHN) by introducing bulky alkyl side chains was reported. Poly(2,6-dialkoxy-1,5-naphthylene)s (PDANs) were prepared by the O -alkylation of PDHN with alkyl halides. The ε values of PDANs at 10 GHz decreased as the length and size of side chains increased. Especially, PDCHMN exhibited the lowest dielectric constant ( ε = 2.29). The ε value results were also supported by refractive index measurement. An efficient method to decrease dielectric constant ( ɛ ) of poly(2,6-dihydroxy-1,5-naphthylene) (PDHN) by introducing bulky alkyl side chains was reported. Poly(2,6-dialkoxy-1,5-naphthylene)s (PDANs) were prepared by the O -alkylation of PDHN with alkyl halides. The ɛ values of PDANs at 10 GHz decreased as the length and size of side chains increased. Especially, PDCHMN exhibited the lowest dielectric constant ( ɛ = 2.29). The ε value results were also supported by refractive index measurement.