Analysis of resistance of T91 steel under load in liquid PbBi

This paper describes behaviour of the ferritic-martensitic steel T91 after long-term exposure in liquid eutectic PbBi. Small specimens of the steel were pre-loaded according to the ISO Standard No. 7539-2 and subsequently exposed to PbBi. The experiment was carried out in a flowing and static liquid...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Korose a ochrana materiálu 2017-12, Vol.61 (5), p.185-190
Hauptverfasser:	Rozumová, L., Di Gabriele, F., Hojná, A.
Format:	Artikel
Sprache:	eng
Schlagworte:	Crack initiation Exposure Ferritic stainless steels Heat resistant steels Martensitic stainless steels
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	This paper describes behaviour of the ferritic-martensitic steel T91 after long-term exposure in liquid eutectic PbBi. Small specimens of the steel were pre-loaded according to the ISO Standard No. 7539-2 and subsequently exposed to PbBi. The experiment was carried out in a flowing and static liquid metal medium at 350°C. The experimental time was selected for the flowing environment at 1000 hours and for static environment at 2000 hours. After exposure, the specimens were analysed by use SEM and EDX. Surface changes of the specimens from different experimental conditions were compared and discussed. The initiation of the cracks wasn´t observed in the monitored expositions.
ISSN:	1804-1213 0452-599X 1804-1213
DOI:	10.1515/kom-2017-0024