Template-free hydrothermal synthesis of beaded nanochain bundles of ZnO and their application as photoanode in dye-sensitized solar cells

ZnO shows promising candidature as photoanode material for dye-sensitized solar cells (DSSCs) due to its high bulk electron mobility and easily tailorable geometrical structures. The objective of this study is to facilitate the development of highly porous hierarchical ZnO for enhanced power conversion efficiency in dye-sensitized solar cells (DSSC) due to its greater dye adsorption. This study investigated the influence of reaction temperatures of 120 °C (sample Z-1) and 180 °C (sample Z-2) in hydrothermal synthesis on structural, morphological and optical properties of resultant ZnO nanostructures and their performance as photoanode material in DSSCs. The synthesized beaded nanochain bundles of ZnO, with multilayered and highly ordered texture, have diameters of several micrometers. Structural and morphological analysis shows that the ZnO beaded nanochain-like architectures possess wurtzite crystalline nature. These morphological improvements (beaded nanochains) of ZnO were found to exhibit higher dye loading and conversion efficiency due to increase in the surface area while reducing charge recombination. The maximum conversion efficiency was obtained with Z-1 and Z-2 is 2.95 and 3.56% with photocurrent of 7.73 and 9.24 mA/cm 2 , respectively. The obtained results pertaining to the DSSC performance studies were corroborated by the impedance spectroscopy data. Graphical abstract Hierarchical beaded ZnO nanochains synthesized at different hydrothermal reaction temperatures of 120 and 180 °C were used as photoanode in DSSCs (probably for the first time) exhibited enhanced light harvesting characteristics (efficiencies of 2.95 and 3.56%, respectively) than the commercial ZnO.