Biodegradable poly(lactic acid)/poly(butylene succinate)/wood flour composites: Physical and morphological properties

This work sought to improve the toughness and thermal stability of poly(lactic acid) (PLA) by incorporating poly(butylene succinate) (PBS) and wood flour (WF). The PLA/PBS blends showed a PBS‐dose‐dependent increase in the impact strength, elongation at break, degree of crystallinity, and thermal st...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Polymer composites 2017-12, Vol.38 (12), p.2841-2851
Hauptverfasser: Chuayjuljit, Saowaroj, Wongwaiwattanakul, Chutima, Chaiwutthinan, Phasawat, Prasassarakich, Pattarapan
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:This work sought to improve the toughness and thermal stability of poly(lactic acid) (PLA) by incorporating poly(butylene succinate) (PBS) and wood flour (WF). The PLA/PBS blends showed a PBS‐dose‐dependent increase in the impact strength, elongation at break, degree of crystallinity, and thermal stability compared to the PLA, but the tensile strength, Young's modulus, and flexural strength were all decreased with increasing PBS content. Based on the optimum impact strength and elongation at break, the 70/30 (w/w) PLA/PBS blend was selected for preparing composites with five loadings of WF (5–30 phr). The impact strength, tensile strength, flexural strength, and thermal stability of the PLA/PBS/WF composites decreased with increasing WF content, and the degree of crystallinity was slightly increased compared to the 70/30 (w/w) PLA/PBS blend. Based on differential scanning calorimetry, the inclusion of PBS and WF into PLA did not significantly change the glass transition and melting temperatures of PLA in the PLA/PBS blends and PLA/PBS/WF composites. From the observed cold crystallization temperature of PLA in the samples, it was evident that the degree of crystallinity of PLA in all the blends and composites was higher than that of PLA. The PLA/PBS blend and PLA/PBS/WF composite degraded faster than PLA during three months in natural soil, which was due to the fast degradation rate of PBS. POLYM. COMPOS., 38:2841–2851, 2017. © 2016 Society of Plastics Engineers