On the stored energy evolution after accumulative roll-bonding of invar alloy

The evolution of stored energy associated with Brass {110} , Copper {112} , S {231} and Cube {001} texture components of Fe-36Ni (wt.%) Invar alloy after accumulative roll-bonding (ARB) processing up to 6 cycles was investigated using two methods: Neutron Diffraction peak broadening analysis and Kernel Average Misorientation (KAM) in an electron backscatter diffraction (EBSD). Both methods evidence the stored energy evolution variation as ECopper > ES > EBrass > ECube. The stored energy increases first with strain up to 3 cycles and then decreases and then slightly rises up again between 4 and 6 cycles but with a trend towards stabilization. The overall evolution of the stored energy versus strain was related to the dislocation density and substructure evolution as well as recovery process. The small increase of the stored energy at high deformation levels is due to the production of new dislocations. Comparisons between results obtained with the two methods and with Dillamore approach show that Geometrically Necessary Dislocations (GND) dislocations in the cells/sub-grains walls are the principal contributor to the stored energy of the alloy. •The stored energy of the texture components vary as Ecopper > ES > EBrass > ECube.•Stored energy evolution was related to the dislocation density and recovery process.•GND dislocations in the cells walls are responsible for the stored energy value.