Warm tempforming effect on the hydrogen embrittlement of 1.8-GPa-class ultra-high-strength low-alloy steel

Hydrogen embrittlement properties were investigated for 1.8-GPa-class ultra-high strength low-alloy steels by means of slow-strain-rate test of the pre-hydrogen-charged notched specimens, accelerated atmospheric corrosion test, and thermal desorption spectrometry. A Mo-bearing steel with a chemical composition of Fe-0.4C-2Si-1Cr-1Mo (mass%) was quenched and tempered at 773K for 1h and then deformed by multi-pass caliber rolling with a cumulative rolling reduction of 76% at 773K to create an ultrafine elongated grain structure with a strong //rolling direction fiber texture. The warm tempformed (TF) sample was subsequently annealed for 1h to clarify the hydrogen trapping effect of nanoscale carbides relative to additive Mo. When the TF sample was annealed at 843K (TFA sample), the hydrogen absorption capacity was enhanced significantly through the formation of nanoscale Mo-rich precipitates in the matrix of ultrafine elongated grains. A high potential for hydrogen embrittlement resistance in an atmospheric corrosion environment was demonstrated in both the TF and TFA samples with an ultra-high tensile strength of 1.8GPa. The TF and TFA samples were much less susceptible to hydrogen embrittlement as compared to the tempered martensitic samples at an ultra-high tensile strength of 1.8GPa. The hydrogen trapping states and the high resistance to hydrogen embrittlement in the TF and TFA samples are discussed in association with the anisotropic, ultrafine grained structures with the nanoscale Mo-rich precipitates.