Effect of bainitic transformation during BQ&P process on the mechanical properties in an ultrahigh strength Mn-Si-Cr-C steel
A medium carbon Mn-Si-Cr alloyed steel was treated by a novel bainite-based quenching and partitioning (BQ&P) process: after full austenization, the steel was firstly austempered at 300°C, 320°C, 340°C, 360°C and 380°C for 30min, and then quenched to 120°C, followed by partitioning at 360°C for...
Gespeichert in:
Veröffentlicht in: | Materials science & engineering. A, Structural materials : properties, microstructure and processing Structural materials : properties, microstructure and processing, 2017-01, Vol.684, p.598-605 |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | A medium carbon Mn-Si-Cr alloyed steel was treated by a novel bainite-based quenching and partitioning (BQ&P) process: after full austenization, the steel was firstly austempered at 300°C, 320°C, 340°C, 360°C and 380°C for 30min, and then quenched to 120°C, followed by partitioning at 360°C for 45min. The multiphase microstructures containing carbide-free bainite (CFB, bainitic ferrite lath plus filmy retained austenite), martensite and retained austenite were characterized by optical microscope, scanning electron microscopy, transmission electron microscopy, X-ray diffraction and dilatometer analysis. An optimum combination of strength and ductility was achieved in the BQ&P steel when the bainitic austempering temperature is 360°C (ultimate tensile strength: 1495MPa; uniform elongation and total elongation: 26.2% and 31.8%; the reduction of area: 47.9%). Besides the transformation-induced plasticity effect of the retained austenite and the composite effect of the multiphase after BQ&P treatment, the formation of carbide free bainite also plays a significant role on the enhanced mechanical properties. The carbide-free bainite could improve the damage resistance of the multiphase due to the additional strain-hardening capacity within the local plasticity deformation zone near the tip of micro-cracks. In this case, the fraction and distribution of CFB should be controlled properly and the macrosegregation should be avoided. |
---|---|
ISSN: | 0921-5093 1873-4936 |
DOI: | 10.1016/j.msea.2016.12.097 |