Ultralow-fired Li2Mg3TiO6-Ca0.8Sr0.2TiO3 composite ceramics with temperature stable at microwave frequency
New temperature stable 4 wt% LiF-doped (1−x)Li2Mg3TiO6-xCa0.8Sr0.2TiO3 (LMT-CST, x = 0.10, 0.15, 0.20, 0.25) composite ceramics were fabricated by solid-state reaction for developing ultra-low temperature (≤800 °C) sintering microwave dielectric ceramics. Sintering temperatures of LMT-CST ceramics w...
Gespeichert in:
Veröffentlicht in: | Journal of alloys and compounds 2017-06, Vol.709, p.299-303 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | New temperature stable 4 wt% LiF-doped (1−x)Li2Mg3TiO6-xCa0.8Sr0.2TiO3 (LMT-CST, x = 0.10, 0.15, 0.20, 0.25) composite ceramics were fabricated by solid-state reaction for developing ultra-low temperature (≤800 °C) sintering microwave dielectric ceramics. Sintering temperatures of LMT-CST ceramics were successfully lowered to 725 °C due to LiF liquid-phase sintering and well-densified microstructures were obtained at 800 °C. Excellent microwave dielectric properties of εr = 18.8, Q × f = 48200 GHz (at 8.2 GHz), τf = 0.3 ppm/°C was obtained at 800 °C for 0.8 LMT-0.2CST-4wt% LiF ceramics. Such sample was compatible with Ag electrodes, which suggests suitability of the developed material for LTCC applications.
•Ultralow-fired LiF-doped Li2Mg3TiO6-Ca0.8Sr0.2TiO3 composite ceramics were prepared.•LiF Addition lowered sintering temperature of LMT-CST ceramics to 725 °C.•The temperature stability of LMT-CST ceramics was improved by adding CST.•A near zero τf values of 0.3 ppm/°C is obtained for LMT-CST ceramics at 800 °C.•Ceramics with well dielectric properties are suitable for LTCC applications. |
---|---|