Diffusion Mechanism for Arsenic in Intrinsic and Extrinsic Conditions in HgCdTe

Due to its low diffusivity and high activation rate, arsenic has become the dopant of choice in p/n HgCdTe high operating temperature technology. Its diffusion mechanism, however, remains imprecise. In this work, arsenic diffusion was studied in molecular beam epitaxy HgCdTe structures consisting of alternatively As-doped and intrinsic layers grown on a CdZnTe substrate. The diffusion coefficient of As was extracted from secondary ion mass spectroscopy concentration profiles. Annealings were performed for different temperatures, mercury partial pressures ( P Hg ), annealing times and cadmium atomic fractions. Fermi-level effect on diffusion was observed, indicating extrinsic conditions for diffusion at high As concentration. Based on the variation of As diffusivity with P Hg and As concentration, we propose that As diffusion occurs on both II and VI sublattices. Our results are consistent with the fact that As VI diffusion is assisted by the Te interstitial, introducing donor levels in the bandgap, while As II diffusion is assisted by the cation vacancy.