Effect of Velocity on the Impact Resistance of Woven Jute Fiber Reinforced Composites

is present project investigated the impact penetration response of woven jute fiber reinforced composites subjected to wide range of low impact velocities. Hand layout woven jute fibers are thermally compressed to ensure no internal defects formed in the composites. Six layers of woven jutes are stacked together using different fiber orientations [0/q/0]s. Low impact velocities are used ranging between 5 – 20 m/s. Force-time, force-displacement and energy-time curves are obtained automatically during the impact tests. The results are then discussed with considering the composite fragmentations and failure mechanisms. It is found that 00 composite orientations capable to absorb sufficiently impact energy for 5 m/s but not for velocity greater than 10 m/s. When fiber orientations used between 15 – 450, the composite impact resistance increased indicating two significant peak forces. These peak forces represent different type of failure mechanisms occurred during the striker progresses.