Investigation of the Expansion of an Oxygen Microwave Remote Plasma for the Growth of Functional Oxide Thin Films

The expansion of an oxygen low-pressure microwave plasma was investigated in order to determine the optimal plasma parameters for the growth of functional oxide semiconductors. Langmuir probe measurements show that the electron density ( n e ) increases with the injected power up to a saturation value of 3.0 × 10 9 cm −3 determined at 10 mTorr while electron temperature ( T e ) remains constant at a value of 1.5 eV. When pressure is varied, n e shows a maximum value at a range from 12 to 20 mTorr while T e decreases monotonously with increasing pressure. In addition, both n e and T e decrease with the axial distance from the plasma source. These effects were discussed through the loss mechanisms in the remote plasma. For a pressure of 13 mTorr and at a substrate temperature of 500 °C, plasma enhanced oxidation of pure metallic Ti thin films lead to the formation of a pure TiO 2 anatase phase compared to a mixed phase of TiO 2 and TiO in the absence of plasma activation. For Mn thin films, the exposure to oxygen remote plasma led to the formation of MnO 2 as opposed to obtaining Mn 3 O 4 when oxidation is performed in the oxygen gas ambient. Remote plasma processing was thus found to provide selective pathways to control oxidation states, stoichiometry and phase composition of technologically attractive oxide thin films.