Preparation and characterization of natural rubber with soft nanomatrix structure

Preparation of natural rubber (NR) with a soft nanomatrix structure was made by graft-copolymerization of butyl acrylate (BA) onto deproteinized natural rubber with tert -butyl hydroperoxide/tetraetylenepentamine in latex stage. The resulting graft-copolymer of deproteinized natural rubber and poly (butyl acrylate) (DPNR- graft -PBA) was characterized by Fourier-transform infrared spectroscopy. Conversion and grafting efficiency of BA were dependent upon BA concentration, which were more than 90 mol% under a suitable condition of the graft-copolymerization. Morphology of DPNR- graft -PBA was observed by transmission electron microscopy after staining film specimens with I 2 vapor for 5 min. The NR particles of about 0.5 μm in diameter were dispersed in PBA matrix of about 15 nm in thickness. Storage modulus and loss tangent of DPNR- graft -PBA were measured, and they were related with the soft nanomatrix structure. The tensile strength and elongation at break decreased as monomer concentration increased.