Very High Cycle Fatigue of Two Ductile Iron Gradesr

Two ductile iron grades, EN-GJS-600-3 a ferritic-pearlitic grade, and EN-GJS-600-10 a silicon strengthened ferritic nodular iron grade, are studied in the very high cycle fatigue range using a 20kHz ultrasonic test equipment. Fatigue strengths and SN-curves are achieved, and fracture surfaces and microstructures are investigated. The ferritic grade with higher ductility displays a lower fatigue strength at 108 load cycles than the ferritic-pearlitic grade, 142 and 167MPa, respectively. Examination of fracture surfaces shows that fatigue failures are controlled by micropores in both of the ductile iron grades, while the graphite nodule distributions do not seem to influence the difference in fatigue strengths. Prediction of the fatigue strengths, using a model for ductile iron proposed by Endo and Yanase, indicates a large potential for improvement in particular for the ferritic grade.