Sensor Performance of Nanostructured TiO2-Cr^sub 2^O3 Thin Films Derived by a Particulate Sol-Gel Route with Various Cr:Ti Molar Ratios

(ProQuest: ... denotes formulae and/or non-USASCII text omitted; see image) Nanocrystalline and nanostructured TiO2-Cr^sub 2^O3 thin films and powders were prepared by a facile and straightforward aqueous particulate sol-gel route at low temperature of 400°C. The prepared sols showed a narrow partic...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of electronic materials 2014-11, Vol.43 (11), p.3922
Hauptverfasser: Mohammadi, Mr, Fray, Dj
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:(ProQuest: ... denotes formulae and/or non-USASCII text omitted; see image) Nanocrystalline and nanostructured TiO2-Cr^sub 2^O3 thin films and powders were prepared by a facile and straightforward aqueous particulate sol-gel route at low temperature of 400°C. The prepared sols showed a narrow particle size distribution with hydrodynamic diameter in the range of 17.7 nm to 19.0 nm. Moreover, the sols were stable over 4 months, with constant zeta potential measured during this period. The effect of the Cr:Ti molar ratio on the crystallization behavior of the products was studied. X-ray diffraction (XRD) analysis revealed that the powders crystallized at low temperature of 400°C, containing anatase-TiO2, rutile-TiO2, and Cr^sub 2^O3 phases, depending on the annealing temperature and Cr:Ti molar ratio. Furthermore, it was found that Cr^sub 2^O3 retarded the anatase to rutile transformation up to 800°C. The activation energy of crystallite growth was calculated to be in the range of 1.3 kJ/mol to 2.9 kJ/mol. Transmission electron microscopy (TEM) imaging showed that one of the smallest crystallite sizes was obtained for TiO2-Cr^sub 2^O3 binary mixed oxide, being 5 nm at 500°C. Field-emission scanning electron microscopy (FESEM) analysis revealed that the deposited thin films had nanostructured morphology with average grain size in the range of 20 nm to 40 nm at 500°C. Thin films produced under optimized conditions showed excellent microstructural properties for gas sensing applications. They exhibited a remarkable response towards low concentrations of NO2 gas at low operating temperature of 200°C, resulting in increased thermal stability of sensing films as well as a decrease in their power consumption. Furthermore, calibration curves revealed that TiO2-Cr^sub 2^O3 sensors followed the power law ... (where S is the sensor response, the coefficients A and B are constants, and [gas] is the gas concentration) for two types of gas, exhibiting excellent capability for detection of low gas concentrations.[PUBLICATION ABSTRACT]
ISSN:0361-5235
1543-186X
DOI:10.1007/s11664-014-3301-4