Influence of CNF content on microstructure and fracture toughness of CNF/alumina composites

Dense 0.4–5.0 wt % carbon nanofiber (CNF)/alumina composites were fabricated by plasma activated sintering. The microstructure—particularly the CNFs distribution—of composites containing different amounts of CNFs was observed in detail, and the influence of the additive amounts of CNF on the microst...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of the Ceramic Society of Japan 2014/04/01, Vol.122(1424), pp.292-299
Hauptverfasser: UEDA, Naoki, YAMAKAMI, Tomohiko, YAMAGUCHI, Tomohiro, USUI, Yuki, AOKI, Kaoru, ENDO, Morinobu, SAITO, Naoto, TARUTA, Seiichi
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Dense 0.4–5.0 wt % carbon nanofiber (CNF)/alumina composites were fabricated by plasma activated sintering. The microstructure—particularly the CNFs distribution—of composites containing different amounts of CNFs was observed in detail, and the influence of the additive amounts of CNF on the microstructure and the fracture toughness of the composites were investigated. The ratio of CNFs distributed individually in the composites decreased with an increase in the addition of CNFs, and the other CNFs formed bundles; notably three-quarters of the CNFs formed bundles in the 5.0 wt % CNF/alumina composite. The alumina grain size distribution of the composites became narrower to smaller grain size side and the average alumina grain size of the composites decreased with an increase in the addition of CNFs from 0.4 to 1.6 wt %. However, the average alumina grain size of the composites did not vary greatly with an increase in the addition of CNFs from 1.6 to 5.0 wt %, because the CNF bundles formed in the 2.5 and 5.0 wt % CNF/alumina composites lowered the grain growth retardation effect of the CNFs. The 1.6 wt % CNF/alumina composite exhibited the highest fracture toughness, because three-fifths of the CNFs distributed individually and uniformly in alumina grain boundaries.
ISSN:1882-0743
1348-6535
DOI:10.2109/jcersj2.122.292