Performance Characteristics of UV-C AlGaN-Based Lasers Grown on Sapphire and Bulk AlN Substrates

The performance characteristics of optically pumped laser heterostructures emitting in the UV-C spectral range between 272 and 279 nm are investigated. The laser heterostructures were grown by metal-organic vapor phase epitaxy on (0001) planar AlN/sapphire, epitaxially laterally overgrown (ELO) AlN/sapphire, and bulk AlN substrates with threading dislocation densities ranging from 2×10 10 to 10 4 cm -2 . We found that the defect density strongly affects the laser performance. The lowest pulse threshold energy density of 50 mJ/cm 2 under resonant optical pumping condition was obtained for an AlGaN multiple quantum well laser grown pseudomorphically on low defect density bulk AlN substrate. Lasing was also observed for AlGaN MQW heterostructures grown on ELO AlN/sapphire templates. The laser emission in all lasers was TE polarized. However, no lasing was observed for heterostructures grown on high defect density AlN/sapphire.