The Solvothermal Synthesis for Nanocrystalline FeIn2S4 at Low Temperature

The Solvothermal Synthesis for Nanocrystalline FeIn2S4 at Low Temperature

5 nm thiospinel FeIn2S4 nanocrystallines were prepared through a solvothermal process at 280 °C. Powder X-ray diffraction (XRD) and transmission electron microscopy (TEM) reveal that the product was nanocrystalline FeIn2S4, with cubic cell, and uniform spherical particle morphology. The factors to t...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Chemistry letters 1999-06, Vol.28 (6), p.481-482
Hauptverfasser: Lu, Qingyi, Hu, Junqing, Tang, Kaibin, Qian, Yitai, Zhou, Guien, Liu, Xianming
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:5 nm thiospinel FeIn2S4 nanocrystallines were prepared through a solvothermal process at 280 °C. Powder X-ray diffraction (XRD) and transmission electron microscopy (TEM) reveal that the product was nanocrystalline FeIn2S4, with cubic cell, and uniform spherical particle morphology. The factors to the formation of uniform FeIn2S4 nanocrystallines with a narrow size distribution were discussed also.
ISSN:0366-7022
1348-0715
DOI:10.1246/cl.1999.481