Translucent alumina with anisotropic-grained microstructure was fabricated utilizing a small amount of glass-forming impurities and the hot isostatic pressing (HIP) method. Its total forward transmission at 600 nm is 72% (1 mm thickness), and bending strength and fracture toughness are estimated to...
Gespeichert in:
Veröffentlicht in: | Journal of the Ceramic Society of Japan 2009, Vol.117(1369), pp.1052-1054 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Translucent alumina with anisotropic-grained microstructure was fabricated utilizing a small amount of glass-forming impurities and the hot isostatic pressing (HIP) method. Its total forward transmission at 600 nm is 72% (1 mm thickness), and bending strength and fracture toughness are estimated to be 649 MPa and 9.4 MPa·m0.5, respectively. Bimodal structure composed of elongated anisotropic-grain and fine equi-axis grain is responsible for the enhancement of mechanical properties. |
---|---|
ISSN: | 1882-0743 1348-6535 |
DOI: | 10.2109/jcersj2.117.1052 |