Preparation and Thermoelectric Properties of p-Type Yb-Filled Skutterudites

p -Type Yb z Fe 4− x Co x Sb 12 skutterudites were prepared by encapsulated melting and hot pressing, and the filling and doping (charge compensation) effects on the transport and thermoelectric properties were examined. The electrical conductivity of all specimens decreased slightly with increasing temperature, indicating that they were in a degenerate state due to high carrier concentrations of 10 20 cm −3 to 10 21 cm −3 . The Hall and Seebeck coefficients exhibited positive signs, indicating that the majority carriers are holes ( p -type). The Seebeck coefficient increased with increasing temperature to maximum values of 100 μ V/K to 150 μ V/K at 823 K. The electrical and thermal conductivities were reduced by substitution of Co for Fe, which was responsible for the decreased carrier concentration. Overall, the Yb-filled Fe-rich skutterudites showed better thermoelectric performance than the Yb-filled Co-rich skutterudites.