Laser Remelting Teratment of Plasma-Sprayed Cr2O3 Oxide Coatings

In the present paper, the influence of laser remelting on the structure and wear resistance of plasma sprayed Cr2O3 oxide coatings is analysed. Sprayed coatings were remelted with the use of cw-CO2 laser. Microstructural investigations were realised with the use of an optical microscope and the SEM method. The texture and phase composition of the coatings were defined with the help of the diffraction method. In addition, the influence of remelting on the wear resistance of plasma sprayed coatings was assessed. The results achieved during the realisation of this work have confirmed the effectiveness of the applied surface treatment, which was expressed by beneficial changes in the structure and the properties of Cr2O3 oxide coatings. W pracy dokonano analizy wpływu laserowego przetapiania na strukturę i odporność na zużycie powłok tlenkowych Cr2O3 natryskiwanych plazmowo. Powłoki natryskiwane zostały przetopione przy użyciu lasera CO2 o ciągłej charakterystyce pracy. Badania mikrostrukturalne realizowano za pomocą mikroskopu optycznego i metody SEM. Teksturę i skład fazowy powłok określono za pomocą metody dyfrakcji rentgenowskiej. Dokonano ponadto oceny wpływu obróbki przetopienowej na odporność na zużycie powłok natryskiwanych plazmowo. Uzyskane w ramach pracy rezultaty potwierdziły skuteczność zastosowanej obróbki powierzchniowej, czego wyrazem były korzystne zmiany w strukturze i własnościach powłok tlenkowych Cr2O3.