Effects of B and Cu Addition and Cooling Rate on Microstructure and Mechanical Properties in Low-Carbon, High-Strength Bainitic Steels

The effects of B and Cu addition and cooling rate on microstructure and mechanical properties of low-carbon, high-strength bainitic steels were investigated in this study. The steel specimens were composed mostly of bainitic ferrite, together with small amounts of acicular ferrite, granular bainite, and martensite. The yield and tensile strengths of all the specimens were higher than 1000 MPa and 1150 MPa, respectively, whereas the upper shelf energy was higher than 160 J and energy transition temperature was lower than 208 K (–65 °C) in most specimens. The slow-cooled specimens tended to have the lower strengths, higher elongation, and lower energy transition temperature than the fast-cooled specimens. The Charpy notch toughness was improved with increasing volume fraction of acicular ferrite because acicular ferrites favorably worked for Charpy notch toughness even when other low-toughness microstructures such as bainitic ferrite and martensite were mixed together. To develop high-strength bainitic steels with an excellent combination of strength and toughness, the formation of bainitic microstructures mixed with acicular ferrite was needed, and the formation of granular bainite was prevented.