The crystal structure and coercive force of SmCo5 sintered permanent magnets

The results of a X‐ray diffraction study of SmCo5 phase homogeneity region boundaries in cast and sintered alloys is presented. Decreasing the temperature from 1200 to 800 °C the solubility of Sm in SmCo5 phase rises monotonously in the (SmCo5 + Sm2Co7) phase region as well as in the (SmCo5 + Sm2Co17) phase region. The decomposition of the solid solution enriched in Co at a temperature below the homogeneity region boundary results in precipitation of the Sm2Co17 phase having the Th2Zn17 crystal structure. In the present paper the high coercivity (IHc = 20 kOe) is obtained in sintered alloys enriched in Co. The alloys enriched in Sm have a coercive force IHc = 30 kOe. The results allow to conclude that in the high coercive state the alloys enriched in Co have a heterogeneous two‐phase crystal structure. Die Ergebnisse einer Röntgenbeugungsuntersuchung der SmCo5‐Phasenhomogenitätsbereichsgrenzen in gegossenen und gesinterten Legierungen werden mitgeteilt. Mit Absenken der Temperatur von 1200 auf 800 °C nimmt die Löslichkeit von Sm in der SmCo5‐Phase monoton sowohl im (SmCo5 + Sm2Co7)‐Phasenbereich als auch im (SmCo5 + Sm2Co17)‐Phasenbereich zu. Der Zerfall der mit Co angereicherten Legierungen bei Temperaturen unterhalb der Homogenitätsbereichsgrenze führt zur Präzipitation der Sm2Co17‐Phase mit Th2Zn17‐Kristallstruktur. In der vorliegenden Arbeit wird die hohe Koerzitivkraft (IHc = 20 kOe) in mit Co angereicherten gesinterten Legierungen erhalten. Die mit Sm angereicherten Legierungen haben eine Koerzitivkraft IHc, = 30kOe. Die Ergebnisse erlauben den Schluß, daß im Hochkoerzitivkraftzustand in Co‐angereicherten Legierungen eine heterogene Zweiphasen‐Kristallstruktur vorhanden ist.