Characterization of dielectric and electro-optic properties of PLZT 9/65/35 films on sapphire for electro-optic applications

Lead lanthanum zirconate titanate (PLZT) thin films were deposited on r-plane sapphire at low temperatures by RF triode magnetron sputtering using lead compensated hot-pressed targets. To obtain fully perovskite phase in the films, two types of post-deposition processing were investigated: rapid the...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	IEEE transactions on ultrasonics, ferroelectrics, and frequency control ferroelectrics, and frequency control, 1998-07, Vol.45 (4), p.1105-1112
Hauptverfasser:	Tunaboylu, B., Harvey, P., Esener, S.C.
Format:	Artikel
Sprache:	eng
Schlagworte:	Condensed matter: electronic structure, electrical, magnetic, and optical properties Dielectric losses Dielectric thin films Electrooptical effects Exact sciences and technology Fundamental areas of phenomenology (including applications) Furnaces Lanthanum Optical elements, devices, and systems Optical films Optical processors, correlators, and modulators Optical properties and condensed-matter spectroscopy and other interactions of matter with particles and radiation Optical properties of bulk materials and thin films Optics Physics Radio frequency Rapid thermal annealing Sputtering Temperature Titanium compounds
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	Lead lanthanum zirconate titanate (PLZT) thin films were deposited on r-plane sapphire at low temperatures by RF triode magnetron sputtering using lead compensated hot-pressed targets. To obtain fully perovskite phase in the films, two types of post-deposition processing were investigated: rapid thermal annealing (RTA) and furnace annealing (FA). Dielectric and electro-optic properties of PLZT films were found to be strongly dependent on annealing conditions. The peak dielectric constant of the films were 1200 and 2800 with Curie temperatures of 110/spl deg/C and 190/spl deg/C after RTA and FA processing, respectively. The dielectric losses in the films were fairly low; tan deltas were less than 0.02 after RTA and less than 0.04 after FA processing. The films showed good optical transmission characteristics after annealing and an anomalously large effective quadratic electro-optic effect was observed in one furnace annealed film.
ISSN:	0885-3010 1525-8955
DOI:	10.1109/58.710594