Structural and electrical properties of polyaniline/silver nanocomposites

Polyaniline (PANI)/Ag nanocomposites were prepared by separate synthesis of silver nanoparticles by inert gas condensation, incorporating in the 1-methyl-2-pyrrolidinone (NMP) solution of polyaniline emeraldine base (PANIEB) and then cast into films at 120 deg C. X-ray diffraction confirmed the presence of ~67 nm silver nanoparticles in the polyaniline matrix. From the thermogravimetric analysis it is observed that the nanocomposite films have a higher degradation temperature than the pure PANI film. Scanning electron microscopy showed a uniform distribution, with spherical and granular morphology for low concentration of Ag nanoparticles, whereas for higher concentration (1.0% Ag) nanorods are formed. The impedance spectroscopic studies of NMP plasticized nanocomposite films suggest microphase separation into reduced and oxidized repeat units. Incorporation of silver nanoparticles in PANI reduces the charge trapping centres and increases the conducting channels, which causes a tenfold decrease in the real part of impedance.