Study for the prediction of the long-term durability of seismic isolators

The application of seismic rubber isolators is considered as one of the steps in assuring the reliability and safe operation of the Fast Breeder Reactor Plant. In order to propose a precise test method for estimating the durability of seismic isolators, we examined the depth-dependent profiles of tensile properties in thick natural rubber blocks after thermal aging at 60-100[degrees]C. The results of this study established the following conclusions: After thermal aging, the rubber blocks exhibited heterogeneous degradation behavior. These rubber blocks could be divided into two areas, the oxidative degraded area near the surface showing large changes in the properties, and the thermal degraded area in the interior showing small property changes. It was established that the depth of oxidation showed temperature dependence, with greater depth of oxidation at lower temperatures. There was also found to be a linear relationship between the logarithm of the depth of oxidation and the reciprocal of the absolute temperature. As a result, the depths of oxidation at normal temperature may be estimated to depths of 6-10 cm. Having calculated the activation energy at depths of 2 mm each from the surface in the oxidative degraded area, it was found that the activation energy held a fixed value independent of depth. 7 refs., 6 figs., 2 tabs.