Strategically designed metal-free deep-ultraviolet birefringent crystals with superior optical properties

Finding new birefringent materials with deep-ultraviolet (DUV, λ < 200 nm) transparency is urgent, as current commercial materials cannot meet the rapidly growing demands in related application fields. Herein, three guanidinium-based compounds, C(NH 2 ) 3 CH 3 SO 3 , β-C(NH 2 ) 3 Cl, and γ-C(NH 2 ) 3 Cl, all featuring [C(NH 2 ) 3 ·X] ∞ (X = CH 3 SO 3 and Cl) pseudo layers, were designed through structural motif tailoring. Theoretical calculations indicate that these metal-free compounds all possess broad bandgaps (6.49-6.71 eV, HSE06) and remarkable birefringence (cal. 0.166-0.211 @ 1064 nm). Centimeter-sized C(NH 2 ) 3 CH 3 SO 3 crystals have been grown using a feasible aqua-solution method. Subsequently, to further optimize the properties, β/γ-C(NH 2 ) 3 Cl was remolded by further tailoring the [C(NH 2 ) 3 ] + cationic unit and the acceptor Cl − anion, and then the fourth compound NH 2 COF was theoretically constructed. Interestingly, NH 2 COF exhibits the desired coexistence of a wider bandgap (7.87 eV, HSE06) and giant birefringence (cal. 0.241 @ 1064 nm) attributed to its higher density of well-aligned birefringence-active groups (BAGs). Furthermore, among these four designed compounds, C(NH 2 ) 3 CH 3 SO 3 has been experimentally synthesized and exhibits a short UV cutoff edge. Centimeter-sized crystals have been grown using a feasible aqueous solution method. This study provides an effective strategy to optimize the density of BAGs for large birefringence and offers valuable insights into the strategic design of metal-free DUV birefringent crystals. Four metal-free deep-ultraviolet birefringent crystals, exhibiting excellent optical properties were designed using Sr 2 Be 2 B 2 O 7 as template, and centimeter-sized C(NH 2 ) 3 CH 3 SO 3 crystals were successfully grown via a mild aqua-solution method.