Organically Modified Nanoclay and Aluminum Hydroxide Incorporated Bionanocomposites towards Enhancement of Physico-mechanical and Thermal Properties of Lignocellulosic Structural Reinforcement

A range of bio-nanocomposites were prepared by incorporation of organo modified montmorillonite nanoclay (OMMT) with or without use of aluminum hydroxide (Al(OH) 3 ) within polylactic acid (PLA) solution. Furthermore, the solution was employed for modification of ligno-cellulosic (jute) fabric structural reinforcements. The successful incorporation of nanofillers within the host polymer, polylactic acid (PLA) was confirmed by Fourier-transform infrared spectroscopy (FT-IR). Water uptake and swelling behaviour studies revealed that the water uptake and swelling ratio of bio-composites reduced significantly as compared to pristine jute fabric, whereas upon incorporation of OMMT and Al(OH) 3 , the water barrier properties reduced even further in the developed bio-nanocomposites. The flexural strength of the bio-nanocomposites also showed improved mechanical and dimensional stability. Synergistic effects of OMMT and Al(OH) 3 were observed in enhancing the aforementioned physico-mechanical properties. Scanning electron microscopy (SEM) studies revealed microstructural details of developed samples. Similarly, the thermo-gravimetric analysis and linear burning rate studies of Al(OH) 3 treated bio-nanocomposite materials revealed enhanced thermal resistance and reduced flammability respectively compared to both pristine woven jute fabric and fabrics treated with PLA alone or those without Al(OH) 3 . From the above results it can safely be said that the bio-nanocomposite material can be a prospective candidate for development of flame retardant biopackaging.