The combined effect of resorcinol/catalyst (100≤R/C≤800) and resorcinol/water (0.04≤R/W≤0.13) molar ratio on the textural and capacitive properties of carbon aerogels with potential application for capacitive deionization has been evaluated. Activated and pyrolyzed aerogels were synthesized by the sol-gel polymerization of resorcinol-formaldehyde mixtures and dried in supercritical conditions. Data show that high R/C and R/W molar ratios lead to materials with large pores in the mesopore range, whereas the surface area and micropore volumes remain somewhat the same. The activation of the aerogels increased the differences in the specific surface and micropore volumes due to the development of microporosity. This effect was more remarkable for the samples with low R/C whatever the R/W ratio, indicating that the carbon aerogel obtained using high amounts of catalyst are more prone to be activated. Regarding the electrochemical features of the aerogels, low capacitance values were measured in aerogels combining low R/W and high R/C and reciprocally low R/C and high R/W molar ratios, due to their higher resistance. Polarization resistances were found to be slightly higher for the pyrolyzed than for activated aerogels, and followed a decreasing trend with the mesoporosity, indicating the outstanding contribution of the mesoporous network to provide a good kinetic response. The desalting capacity of monolithic aerogels showed a simultaneous dependence with the surface area and the resistivity of the electrodes, pointing out the importance of performing electrochemical measurements in adequate cell configurations (i.e., desalting units) upon the intended application. The textural properties of carbon aerogels are strongly influenced by the synthesis parameters precursor to catalyst (R/C) and water (R/C) ratios. The volumetric capacitance measured in a symmetric cell with monolithic electrodes of carbon aerogel strongly correlates with both surface area and electrical resistivity [Display omitted] •Influence of the synthesis conditions on the properties of carbon aerogels is reported.•Specific surface decreases in the activated samples when either R/C or R/W increase.•An enhanced decrease of the capacitance was observed when R/C and R/W increase.•Ohmic resistance of the electrodes that strongly depends on the R/W and R/C.•Electrosorption capacity is successfully correlated to surface area and resistivity.