Investigation of multiferroic behavior on flakes-like BiFeO{sub 3}

In present work, multiferroic BiFeO{sub 3} was synthesized by hydrothermal route. The rhombohedral structure was confirmed X-ray diffraction pattern and data fitted with Reitveld refinement using Full-Prof software suite. SEM micrograph shows flake like morphology. Frequency and temperature dependen...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:AIP conference proceedings 2016-05, Vol.1731 (1)
Hauptverfasser: Sheikh, Javed R., Gaikwad, Vishwajit M., Acharya, Smita A.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In present work, multiferroic BiFeO{sub 3} was synthesized by hydrothermal route. The rhombohedral structure was confirmed X-ray diffraction pattern and data fitted with Reitveld refinement using Full-Prof software suite. SEM micrograph shows flake like morphology. Frequency and temperature dependence of dielectric constant and dielectric loss were studied and detected enhancement in dielectric constant. The magnetic measurement indicates antiferromagnetic nature of BFO. P-E curve shows ferroelectic hysteresis loop with remanent polarization (2Pr) 0.3518 µC/cm{sup 2}. The dielectric anomaly observed near T{sub N} can be assigned to magnetoelectric coupling which is useful in device application.
ISSN:0094-243X
1551-7616
DOI:10.1063/1.4948196