Structural and optical analysis on europium doped AZrO{sub 3} (A=Ba, Ca, Sr) phosphor for display devices application

Behavior displayed by europium doped AZrO{sub 3} phosphor which was synthesized by solid state reaction method. For synthesis of BaZrO{sub 3}, SrZrO{sub 3} and CaZrO{sub 3} phosphor with fixed concentration of europium ion was calcination at 1000°C and sintered at 1300°C following intermediate grinding. Synthesized sample was characterized by X-ray diffraction analysis and crystallite sized was calculated by Scherer’s formula. From PL spectra of prepared phosphors shows intense emission centred at 612nm (red emission) with high intensity for SrZrO{sub 3}:Eu{sup 3+}. For europium doped BaZrO{sub 3} and CaZrO{sub 3} (613nm) phosphor shows less intense PL spectra as compared to SrZrO{sub 3}:Eu{sup 3+}. The strong emission peak of AZrO{sub 3}:Eu{sup 3+} phosphor is due to forced electric dipole transition of {sup 5}D{sub 0} to {sup 7}F{sub 2} centered at 612 and 613nm. It is characteristic red emission for europium ion. The excitation spectra of AZrO{sub 3}:Eu{sup 3+} phosphor mainly consists of the charge transfer and (CTB) of Eu{sup 3+} located in 200–350 nm centred at 254nm. The present phosphors can act as single host for red light emission in display devices. The CIE coordinates were calculated by Spectrophotometric method using the spectral energy distribution of the AZrO{sub 3}:Eu{sup 3+} sample.