Study of the microstructure evolution of heat treated Ti-rich NiTi shape memory alloy

Martensitic evolution in Ti-rich NiTi alloy, Ti50.5Ni49.5, has been investigated as a function of annealing, solution treatment and a combination thereof and a detailed electron microscopic investigation carried out. Self-accommodated martensite plates resulted in all heat treated samples. Martensitic type II twins, which are common in NiTi shape memory alloys, was found in both as-received and heat-treated samples. Solution treated samples, additionally, showed {11-1} type I twinning was also found in samples that have been annealed after solution-treatment. Another common feature of the microstructure in both as-received and heat treated samples is the formation of Ti2Ni precipitates. The size, number and dispersions of these precipitates can be controlled by resorting to a suitable heat treatment e.g. solution treatment.