Rechargable xLi{sub 2}MnO{sub 3}·(1 − x)Li{sub 4/3}Mn{sub 5/3}O{sub 4} electrode nanocomposite material as a modification product of chemical manganese dioxide by lithium additives

Highlights: • Li-ion battery cathode preparation procedure included MnO{sub 2} modification by Li-salts with subsequent heat treatment. • Li{sub 4}Mn{sub 5}O{sub 12}, Li{sub 2}MnO{sub 3,} and Li-rich phases form active nanocomposite cathode. • Heat treatment mode is of crucial importance for rechargeability. • Cathode material capacity is 150 mA h g{sup −1} within 2.5–4.5 V. - Abstract: Relatively simple preparation procedure of rechargeable Li-ion battery cathode material via manganese dioxide treatment with Li-containing additive and subsequent calcination has been demonstrated. X-ray diffraction, infrared spectroscopy, thermogravimetric analysis, and atomic force microscopy study were characterisation methods of modification products. Pyrolusite, Li{sub 0.3}MnO{sub 2}, layered Li{sub 2}MnO{sub 3}, and spinel Li{sub 4}Mn{sub 5}O{sub 12} phases were revealed as products of initial ramsdellite phase transformations at temperatures of heat treatment ranging from 360 °C to 600 °C. Optimal temperature of final heat treatment from the point of view of rechargeability and discharge characteristics was 450 °C. Samples heat-treated at 450 °C are characterized by the unique combination of Li{sub 4/3}Mn{sub 5/3}O{sub 4} and Li{sub 2}MnO{sub 3} phase components due to their structural integration, a significant degree of disordering, and sizes of nanocrystallites with Li diffusion path, which is the most favourable for reversibility. The prepared nanocomposite cathode material delivers a capacity of 150 mA h g{sup −1} within 2.5–4.5 V at 0.1 mA discharge.