Spectral evolution of Eu{sup 3+} doped Y{sub 3}NbO{sub 7} niobate induced by temperature

A Eu{sup 3+} doped Y{sub 3}NbO{sub 7} niobate powder was synthetized using a polymerizable complex route. It gave rise to nanometric particles that crystallized in the fluorine structure, corresponding to the Y{sub 3}NbO{sub 7} phase. The thermal evolution of this powder was followed up to 1600 °C, using X-ray diffraction and optical characterizations. The fluorine structure was maintained in the whole temperature range. However, spectral evolution of the samples calcined above 900 °C showed a more complex situation. Emission spectra of powders heat treated at different temperatures showed an evolution of the emission lines that can be attributed first to a better crystallization of the niobate phase and second to its partial decomposition in favor of the formation of YNbO{sub 4} and Y{sub 2}O{sub 3}. Although the Y{sub 3}NbO{sub 7} phase appeared stable up to 1650 °C, from X-ray diffraction analysis, spectral analysis showed that the local environment of the doping element is modified from 1100 °C. - Graphical abstract: Spectral evolution of Eu{sup 3+} doped Y{sub 3}NbO{sub 7} niobate induced by temperature.