The solubility and site preference of Fe{sup 3+} in Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnets

A series of Fe{sup 3+}-bearing Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} (LLZO) garnets was synthesized using solid-state synthesis methods. The synthetic products were characterized compositionally using electron microprobe analysis and inductively coupled plasma optical emission spectroscopy (ICP-OES) and structurally using X-ray powder diffraction and {sup 57}Fe Mössbauer spectroscopy. A maximum of about 0.25 Fe{sup 3+} pfu could be incorporated in Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnet solid solutions. At Fe{sup 3+} concentrations lower than about 0.16 pfu, both tetragonal and cubic garnets were obtained in the synthesis experiments. X-ray powder diffraction analysis showed only a garnet phase for syntheses with starting materials having intended Fe{sup 3+} contents lower than 0.52 Fe{sup 3+} pfu. Back-scattered electron images made with an electron microprobe also showed no phase other than garnet for these compositions. The lattice parameter, a{sub 0}, for all solid-solution garnets is similar with a value of a{sub 0}≈12.98 Å regardless of the amount of Fe{sup 3+}. {sup 57}Fe Mössbauer spectroscopic measurements indicate the presence of poorly- or nano-crystalline FeLaO{sub 3} in syntheses with Fe{sup 3+} contents greater than 0.16 Fe{sup 3+} pfu. The composition of different phase pure Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnets, as determined by electron microprobe (Fe, La, Zr) and ICP-OES (Li) measurements, give Li{sub 6.89}Fe{sub 0.03}La{sub 3.05}Zr{sub 2.01}O{sub 12}, Li{sub 6.66}Fe{sub 0.06}La{sub 3.06}Zr{sub 2.01}O{sub 12}, Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12}, and Li{sub 6.19}Fe{sub 0.19}La{sub 3.02}Zr{sub 2.04}O{sub 12}. The {sup 57}Fe Mössbauer spectrum of cubic Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12} garnet indicates that most Fe{sup 3+} occurs at the special crystallographic 24d position, which is the standard tetrahedrally coordinated site in garnet. Fe{sup 3+} in smaller amounts occurs at a general 96h site, which is only present for certain Li-oxide garnets, and in Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12} this Fe{sup 3+} has a distorted 4-fold coordination. - Graphical abstract: Cubic nominally Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} (LLZO) garnet is a promising candidate to be used as a solid electrolyte in Li-ion batteries. A series of Fe{sup 3+}-bearing LLZO garnets was synthesized and characterized compositionally and structurally. {sup 57}Mössbauer measu