Searching for “LiCr{sup II}PO{sub 4}”
The two new phosphates LiCr{sup II}{sub 4}(PO{sub 4}){sub 3} and Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4} are discovered as equilibrium phases (ϑ=800 °C) in the quarternary system Li/Cr/P/O. Their crystal structures have been determined from single-crystal X-ray diffraction data (LiCr...
Gespeichert in:
Veröffentlicht in: | Journal of solid state chemistry 2014-10, Vol.218 |
---|---|
Hauptverfasser: | , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The two new phosphates LiCr{sup II}{sub 4}(PO{sub 4}){sub 3} and Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4} are discovered as equilibrium phases (ϑ=800 °C) in the quarternary system Li/Cr/P/O. Their crystal structures have been determined from single-crystal X-ray diffraction data (LiCr{sup II}{sub 4}(PO{sub 4}){sub 3}: violet-blue, Pnma (no. 62), Z=4, a=6.175(1) Å, b=14.316(3) Å, c=10.277(2) Å, 100 parameters, R{sub 1}=0.028, wR{sub 2}=0.08, 2060 unique reflections with F{sub o}>4σ(F{sub o}); Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4}: greyish-green, P1{sup ¯} (no. 2), Z=1, a=4.9379(7) Å, b=7.917(2) Å, c=8.426(2) Å, α=109.98(2)°, β=90.71(1)°, γ=104.91(1)°, 131 parameters, R{sub 1}=0.022, wR{sub 2}=0.067, 1594 unique reflections with F{sub o}>4σ(F{sub o})). Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4} adopts an hitherto unknown structure type. The crystal structure of LiCr{sup II}{sub 4}(PO{sub 4}){sub 3} is isotypic to that of NaCd{sup II}{sub 4}(PO{sub 4}){sub 3} and related to that of the mineral silicocarnotite Ca{sub 5}(PO{sub 4}){sub 2}(SiO{sub 4}). Significant disorder between Li{sup +} and Cr{sup 2+} is observed for both crystal structures. The oxidation states assigned to chromium in these two phosphates are in agreement with UV/vis/NIR absorption spectra and magnetic susceptibility data recorded for both compounds. Instead of “LiCr{sup II}PO{sub 4}” mixtures of LiCr{sup II}{sub 4}(PO{sub 4}){sub 3}, Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4}, Cr{sub 2}O{sub 3}, and CrP are observed at equilibrium. Instead of “Li{sub 2}Cr{sup II}P{sub 2}O{sub 7}” four-phase mixtures consisting of Li{sub 9}Cr{sup III}{sub 3}(P{sub 2}O{sub 7}){sub 3}(PO{sub 4}){sub 2}, Li{sub 3}Cr{sup III}{sub 2}(PO{sub 4}){sub 3}, LiCrP{sub 2}O{sub 7}, and CrP were obtained. - Graphical abstract: Investigations on the equilibrium relations in the system Li/Cr/P/O revealed the two hitherto unknown phosphates Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4} and LiCr{sup II}{sub 4}(PO{sub 4}){sub 3}. They form instead of “LiCr{sup II}PO{sub 4}”. The crystal structures, magnetic behavior and optical spectra of these phosphates are reported. - Highlights: • The two new phosphates Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}){sub 4} and LiCr{sup II}{sub 4}(PO{sub 4}){sub 3} have been characterized. • Optical spectra and paramagnetism of the these phosphates are explained by AOM. • Li{sub 5}Cr{sup II}{sub 2}Cr{sup III}(PO{sub 4}) |
---|---|
ISSN: | 0022-4596 1095-726X |
DOI: | 10.1016/J.JSSC.2014.06.020 |