The influence of a silica pillar in lamellar tetratitanate for selective catalytic reduction of NO{sub x} using NH{sub 3}

Highlights: • Potassium ions significantly affected the SCR. • The introduction of silica in the catalyst promotes the NH{sub 3}-SCR reaction. • The catalysts activities were not significantly influenced by SO{sub 2} addition. - Abstract: Silica-pillared layered titanate (SiO{sub 2}–Ti{sub 4}O{sub 9}) was prepared by intercalating organosilanes into the interlayers of a layered K{sub 2}Ti{sub 4}O{sub 9} followed by calcination at 500 °C. The lamellar titanates produced were used as a support to prepare vanadium catalysts (1 and 2 wt%) through wet impregnation for selective catalytic reduction (SCR) of NO. The catalysts were characterized using nitrogen adsorption (BET), X-ray diffraction (XRD), temperature programmed reduction (H{sub 2}-TPR), nuclear magnetic resonance ({sup 29}Si NMR), and infrared spectroscopy (FT-IR). Reduction of NO by NH{sub 3} was studied in a fixed-bed reactor packed with the catalysts and fed a mixture comprising 1% NH{sub 3}, 1% NO, 10% O{sub 2}, and 34 ppm SO{sub 2} (when used) in helium. The results demonstrate that activity is correlated with the support, i.e., with acidic strength of catalysts. The potassium in the support, K{sub 2}Ti{sub 4}O{sub 9}, significantly affected the reaction and level of vanadium species reduction. The catalyst (1VSiT) with 1 wt% vanadium impregnated on the SiO{sub 2}–Ti{sub 4}O{sub 9} support reduced ∼80% of the NO. Approximately the same conversion rate was generated on the catalyst (2VSiT) with 2 wt% vanadium using the same support. The increased NH{sub 3} adsorption demonstrate that introduction of silica in the catalyst promotes the NH{sub 3}-SCR reaction. More importantly, 2VSiT and 1VSiT were strongly resistant to SO{sub 2} poisoning.