Planar ultrananocrystalline diamond field emitter in accelerator radio frequency electron injector: Performance metrics

A case performance study of a planar field emission cathode (FEC) based on nitrogen-incorporated ultrananocrystalline diamond, (N)UNCD, was carried out in an RF 1.3 GHz electron gun. The FEC was a 100 nm (N)UNCD film grown on a 20 mm diameter stainless steel disk with a Mo buffer layer. At surface gradients 45–65 MV/m, peak currents of 1–80 mA (equivalent to 0.3–25 mA/cm{sup 2}) were achieved. Imaging with two YAG screens confirmed emission from the (N)UNCD surface with (1) the beam emittance of 1.5 mm × mrad/mm-rms and (2) longitudinal FWHM and rms widths of non-Gaussian energy spread of 0.7% and 11% at an electron energy of 2 MeV. Current stability was tested over the course of 36 × 10{sup 3} RF pulses (equivalent to 288 × 10{sup 6 }GHz oscillations)