Nanoscale mapping of the W/Si(001) Schottky barrier

The W/Si(001) Schottky barrier was spatially mapped with nanoscale resolution using ballistic electron emission microscopy (BEEM) and ballistic hole emission microscopy (BHEM) using n-type and p-type silicon substrates. The formation of an interfacial tungsten silicide is observed utilizing transmis...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of applied physics 2014-07, Vol.116 (2)
Hauptverfasser: Durcan, Chris A., Balsano, Robert, LaBella, Vincent P.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The W/Si(001) Schottky barrier was spatially mapped with nanoscale resolution using ballistic electron emission microscopy (BEEM) and ballistic hole emission microscopy (BHEM) using n-type and p-type silicon substrates. The formation of an interfacial tungsten silicide is observed utilizing transmission electron microscopy and Rutherford backscattering spectrometry. The BEEM and BHEM spectra are fit utilizing a linearization method based on the power law BEEM model using the Prietsch Ludeke fitting exponent. The aggregate of the Schottky barrier heights from n-type (0.71 eV) and p-type (0.47 eV) silicon agrees with the silicon band gap at 80 K. Spatially resolved maps of the Schottky barrier are generated from grids of 7225 spectra taken over a 1 μm × 1 μm area and provide insight into its homogeneity. Histograms of the barrier heights have a Gaussian component consistent with an interface dipole model and show deviations that are localized in the spatial maps and are attributed to compositional fluctuations, nanoscale defects, and foreign materials.