Structural chemistry and magnetic properties of Nd{sub 18}Li{sub 8}Fe{sub 4}M′O{sub 39} (M′=Al, Ga) and La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39}

Polycrystalline samples of Nd{sub 18}Li{sub 8}Fe{sub 4}M′O{sub 39} (M′=Al, Ga) and La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39} have been prepared by the ceramic method and characterised by neutron diffraction and magnetometry. All three compounds adopt a cubic structure (space group Pm3{sup ¯}n, a ∼12 Å) based on intersecting 〈1 1 1〉 chains of cation sites with alternating octahedral and prismatic coordination geometry. These sites are occupied by Li, Fe and M′ or In; Nd or La cations occupy sites between the chains. The cation distribution over the octahedral and prismatic sites within the chains is disordered in all three compounds. The Nd-containing compositions show spin-glass behaviour below ∼4.5 K whereas small, weakly-ferrimagnetic domains form in La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39} below 7.60 K. The dependence of the magnetic properties on the nature of the lanthanide cation is discussed. - Graphical abstract: At low temperatures Nd{sub 18}Li{sub 8}Fe{sub 4}M′O{sub 39} (M’=Al, Ga) behave as spin glasses whereas small ferrimagnetic domains form in La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39}. Display Omitted - Highlights: • p-Block cations can be accommodated in the La{sub 18}Li{sub 8}Rh{sub 5}O{sub 39} structure. • Small ferrimagnetic domains in La{sub 18}Li{sub 8}Fe{sub 4.5}In{sub 0.5}O{sub 39}. • Magnetic behaviour controlled by the lanthanide cation.