Blue-violet InGaN laser diodes grown on bulk GaN substrates by plasma-assisted molecular-beam epitaxy

We report on the InGaN multiquantum laser diodes (LDs) made by rf plasma-assisted molecular beam epitaxy (PAMBE). The laser operation at 408 nm is demonstrated at room temperature with pulsed current injections using 50 ns pulses at 0.25% duty cycle. The threshold current density and voltage for the...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Applied physics letters 2005-01, Vol.86 (1), p.011114-011114-3
Hauptverfasser: Skierbiszewski, C., Wasilewski, Z. R., Siekacz, M., Feduniewicz, A., Perlin, P., Wisniewski, P., Borysiuk, J., Grzegory, I., Leszczynski, M., Suski, T., Porowski, S.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:We report on the InGaN multiquantum laser diodes (LDs) made by rf plasma-assisted molecular beam epitaxy (PAMBE). The laser operation at 408 nm is demonstrated at room temperature with pulsed current injections using 50 ns pulses at 0.25% duty cycle. The threshold current density and voltage for the LDs with cleaved uncoated mirrors are 12 kA ∕ cm 2 ( 900 mA ) and 9 V , respectively. High output power of 0.83 W is obtained during pulse operation at 3.6 A and 9.6 V bias with the slope efficiency of 0.35 W ∕ A . The laser structures are deposited on the high-pressure-grown low dislocation bulk GaN substrates taking full advantage of the adlayer enhanced lateral diffusion channel for adatoms below the dynamic metallic cover. Our devices compare very favorably to the early laser diodes fabricated using the metalorganic vapor phase epitaxy technique, providing evidence that the relatively low growth temperatures used in this process pose no intrinsic limitations on the quality of the blue optoelectronic components that can be fabricated using PAMBE.
ISSN:0003-6951
1077-3118
DOI:10.1063/1.1846143