Stress-strain response of a cast 319-T6 aluminum under thermomechanical loading

The stress-strain behavior of cast 319-T6 aluminum-copper alloys with three different secondary dendrite arm spacings (SDASs) was studied at high temperatures and under thermomechanical deformation, exposing marked cyclic softening. A two state-variable unified inelastic constitutive model proposed earlier was modified to describe the stress-strain responses of these alloys by considering the variation of hardening and recovery functions of back-stress and drag stress. The SDAS was incorporated in the model as a length-scale parameter, and the material constants were determined systematically from experiments on a cast 319-T6 aluminum with small and large SDASs. The capabilities of the constitutive model were checked by the comparisons of simulations to experiments in the small-strain regime ( < 0.005). The results show that the model provides successful simulations for material response after thermal exposure at high temperature and cyclic transient stress-strain behavior The causes of mechanical behaviors at the macro scale are discussed based on microstructural changes during thermal exposure.