Moisture outgassing from siloxane elastomers containing surface-treated-silica fillers

The outgassing kinetics from siloxane elastomers is dominated by moisture desorption from the reinforcing silica filler and can be detrimental in moisture-sensitive applications. In this study, a custom 3D printable siloxane rubber (LL50) was analyzed in three different states: after a high temperature vacuum heat treatment, limited re-exposure to moisture after vacuum heat treatment, and in the as-received condition. The outgassing kinetics were extracted using isoconversional and iterative regression analyses. Moisture release by physisorbed and chemisorbed water from the samples have activation energies in the range of 50 kJ/mol (physisorbed type) to 220 kJ/mol (chemisorbed type). Overall, moisture outgassing from LL50 was 10 times lower than that from traditionally prepared siloxane rubbers. The vastly diminished moisture content in LL50 is attributed to the existence of a finite low level of silanol groups that remain on the fumed silica surface even after hydrophobic treatment.